Effect of doping polyacrylic acid with some dopants as studied by different techniques

The molecular weight of polyacrylic acid (PAA) was determined by a viscometric method using NaNO₃ as solvent at 30°C. The specific electric conductivities (σ) of PAA as well as PAA doped with carbon black (CB), chromium oxide (Cr₂O₃), and cupferron with different concentrations (from 0.25 to 1 wt %) were measured at a temperature range 360–400 K. IR spectra of some polymers were determined and it was shown that when PAA was doped with 0.5 wt % CB, a C? O? C band appeared at 775–875 cm^?1. The positron annihilation lifetime (PAL) spectra in PAA doped with the above‐mentioned dopants were measured as a function of their concentrations. It was observed that the short lifetime intensity I₁ decreased, whereas the intermediate lifetime intensity I₂, which is related to the conductivity of the material, increased with increasing the wt % of Cr₂O₃ and cupferron as well as at low concentrations of CB. These results are discussed in terms of the conducting island model. It was found that there were distinct positive relationships between σ and I₂. © 2002 John Wiley & Sons, Inc. J Appl Polym Sci 84: 877–883, 2002; DOI 10.1002/app.10381