| 唐钢FTSC工艺板材孔洞缺陷成因及预防措施 |
| |
| 引用本文： | 杨晓江,郝常鑫,张彩东,杨杰,刘广涛,席晓利. 唐钢FTSC工艺板材孔洞缺陷成因及预防措施[J]. 钢铁研究, 2011, 39(2): 51-54 |
| |
| 作者姓名： | 杨晓江 郝常鑫 张彩东 杨杰 刘广涛 席晓利 |
| |
| 作者单位： | 1. 唐山钢铁集团有限责任公司,河北唐山063016;钢铁研究总院连铸技术国家工程研究中心,北京100081
2. 唐山钢铁集团有限责任公司,河北唐山,063016 |
| |
| 摘 要： | 采用金相显微镜和扫描电镜对唐钢FTSC工艺板材孔洞成因进行了分析,结果表明：唐钢SS400热轧材的孔洞是由沿铸坯厚度方向存在中间裂纹造成的。对轻压下时铸坯坯壳厚度的变化进行了分析,发现铸坯中间裂纹源主要在扇形0段,是由于辊子的相互错位而诱发;裂纹源产生后沿铸坯厚度方向延伸形成中间裂纹。通过减小扇形0段的压下量,合理分配到其它扇形段中,减轻或消除了铸坯枝晶间裂纹的产生,抑制了铸坯中间裂纹的生成,避免了板卷孔洞缺陷。
|
| 关 键 词： | 薄板坯 轻压下 裂纹 孔洞 |
Reason analysis and prevention measures of hole formation in strip proudced by FTSC at Tang Steel |
| |
| YANG Xiao-jiang,HAO Chang-xin,ZHANG Cai-dong,YANG Jie,LIU Guang-tao,XI Xiao-li. Reason analysis and prevention measures of hole formation in strip proudced by FTSC at Tang Steel[J]. Research on Iron and Steel, 2011, 39(2): 51-54 |
| |
| Authors: | YANG Xiao-jiang HAO Chang-xin ZHANG Cai-dong YANG Jie LIU Guang-tao XI Xiao-li |
| |
| Affiliation: | 1 (1.Tangshan Iron and steel Co.Ltd,Hebei Iron and Steel Group,Tangshan 063016,China;2.National Engineering and Research Center for Continuous Casting Technology,Central Iron and Steel Research Institute,Beijing 100081,China) |
| |
| Abstract: | The reasons of hole formation in strip produced by FTSC at Tang Steel were analyzed by means of metallographic microscope and SEM.The results reveal that the hole formed in SS400 hot-rolled strip was caused by cracks in center of continuous casting slab rather than by slag entrapment.The shell thickness change during soft reduction was analyzed.The crack source was resulted in mismatch of No.0 rolls on fan-shaped segment,and the crack source evolved into mid-cracks along thickness direction.At last,the reduction was reduced in No.0 fan-shaped segment and allocated to the other fan-shaped segment.The mid-cracks were restrained,and then the hole formation in SS400 hot-rolled strip was avoided. |
| |
| Keywords: | thin slab continuous casting soft reduction crack hole |