Discharge behaviour of plane nickel hydroxide electrodes

Plane nickel oxide electrodes were prepared by electrochemical deposition of nickel hydroxide on flexible nickel strips. Compact and adherent deposits were obtained, with thickness up to 4 × 10^?3 cm. They were cycled in 6 M KOH solution, and owing to the flexibility of the supporting nickel strips, did not show detaching. The results obtained from galvanostatic discharge curves fit the Peukert equation iⁿt = constant, giving an n value of 1.23 for the 1 × 10^?3 cm thick film and a value of 1.10 for the 4 × 10^?3 cm think film. The diffusion coefficients of moving species are in the order of magnitude of 10^?5 ?10^?6 cm²s^?1; the rate of discharge does not seem to be limited by proton diffusion. The proton diffusion in solid phase is not the only factor to be taken into account in the discharge process; diffusion and migration OH^? and H₂O species play an important role in plane thick nickel oxide film discharge.