The effect of hydrogen on the selective catalytic reduction of NO in excess oxygen over Ag/Al2O3

The selective catalytic reduction (SCR) of nitrogen oxides (NO_x) by propane in the presence of H₂ on sol–gel prepared Ag/Al₂O₃ catalysts (0.5–5 wt.% Ag) was investigated. It was confirmed that hydrocarbon-assisted SCR of NO_x is remarkably enhanced by co-feeding hydrogen to a lean exhaust gas mixture (λ>1), attaining considerable activity within a wide temperature window (470–825 K). The samples had marginal activity at 575 K without co-fed H₂, but achieved up to 60% NO_x conversion in the presence of H₂ at a space velocity of 30,000 h^?1. NO₂ as NO_x feed component is not converted to N₂ by C₃H₈ to a substantial extent under lean conditions. This points to an activation route of NO through direct conversion to adsorbed nitrite/nitrate or to a dissociation of NO over Ag⁰, formed through short-term reduction by H₂. The nature of Ag species was characterized by X-ray diffraction, temperature-programmed reduction, pulse thermoanalytical measurements, electron microscopy and FTIR spectroscopy. It could be shown that Ag₂O nano-sized clusters are predominantly present on all samples, whereas formation of silver aluminate could not be confirmed. Nano-sized Ag₂O clusters can reversibly be reduced/reoxidized by H₂. A silver loading higher than 2 wt.% leads to a part of Ag₂O particles, which are thermally decomposed during calcination at 800 K or higher. The catalytic role of this metallic silver is still unclear. Formal kinetic analysis of catalytic data revealed that the activation energy of the overall reaction is significantly lowered in the presence of H₂. The presence of water does not change the activation energy. It is concluded that hydrogen reduces the nano-sized Ag₂O clusters to Ag⁰ on a short-term scale. Zero-valent silver promotes a dissociation pathway of NO_x conversion. The fact that more oxidized ad-species (nitrite/nitrate) are observed in the presence of H₂ is attributed to a dissociative activation of gas-phase oxygen on Ag⁰.