Thermodynamic stability of Na2ZrO3 using the solid electrolyte galvanic cell technique

The sodium potential in the test electrode (a) Pt,O₂,Na₂ZrO₃,ZrO₂ was measured by using the emf technique employing Na-β^″-alumina as the solid electrolyte in conjunction with (b) Pt,O₂,Al₂O₃,NaAl₁₁O₁₇, (c) Pt,O₂,Na₂MoO₄,Na₂Mo₂O₇ and (d) Pt,Na₂CO₃,CO₂,O₂ as the reference electrodes over the ranges 880–1045, 700–800 and 850–940 K, respectively. The emf results between electrodes (b) and (c) were utilized for internal consistency checks. From the results on cells formed between (a) and (b) and those on (a) and (c), the standard Gibbs energy of formation, Δ_fG^o (kJ/mol) of Na₂ZrO₃ was determined to be −1699.4+0.3652T (K) valid over the temperature range 700–1045 K. The break in the emf data at 1045 K was corroborated by independent TG/DTA measurements carried out on Na₂ZrO₃ which exhibited an endotherm at 1055 K indicative of a phase transition in Na₂ZrO₃.