Investigation of doped-gadolinium zirconate nanomaterials for high-temperature hydrogen sensor applications |
| |
Authors: | Christina Wildfire Engin Çiftyürek Katarzyna Sabolsky Edward M. Sabolsky |
| |
Affiliation: | 1. Mechanical and Aerospace Engineering Department, West Virginia University (WVU), Morgantown, WV, 26505, USA
|
| |
Abstract: | The incorporation of selective nanomaterials, such as common metal oxide semiconductor compositions, into resistive-type gas sensors has been shown by many researchers to lead to very high sensitivities and response rates, especially for micro-sized chemical sensors for room-temperature applications. The same strategy utilizing sensing nanomaterials has not been demonstrated for high-temperature sensors due to the intrinsic instability of typical metal oxide semiconductor nanomaterials at temperatures >500 °C. Within this work, doped Gd2Zr2O7 (GZO) nanomaterial compositions were investigated for H2 resistive-type sensors for applications between 600 and 1000 °C. This paper investigates the mechanism of H2 sensing for doped GZO nanomaterials and SnO2/GZO nanocomposites at the elevated temperatures. By integrating 10 vol.% nano-SnO2 into yttrium-doped GZO nanomaterials, a sensitivity of 4.15 % was retained for 4000 ppm H2 levels with a low signal drift of 0.42 %/h at 1000 °C in a 20 % O2/N2 gas stream. The signal drift was reduced by more than half of that compared to pure nano-SnO2 at the same conditions. The nano-GZO limited the grain growth of the nano-SnO2 particles and also prevented the nano-SnO2 from fully reducing to Sn at high temperatures in a low oxygen atmosphere. It is among the first resistive-type sensors operating at 1000 °C with sensing times of <5 min. This demonstration provided an example of a strategy of combining traditional metal oxide semiconductor and refractory nanomaterial compositions to form sensing nanocomposites with new sensing mechanisms, as well as, enhanced chemical and microstructural stabilities in high-temperature environments. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|