Development of recrystallization textures in 0.08%C steel |
| |
Authors: | R. K. Khatirkar S. Nimsarkar P. Das A. Vishwakarma N. Thawale |
| |
Affiliation: | (1) The State Key Laboratory of Rolling and Automation of Northeastern University, Shenyang, 110004, P.R. China;(2) Jinan Iron and Steel Corp., Jinan, China |
| |
Abstract: | The present work investigates the effect of cold deformation on the evolution of microstructure and textures during recrystallization in 0.08%C steel. The cold rolling texture consists of partial α-fiber (RD//〈110〉) and complete γ-fiber (ND//〈111〉) along with Goss ({110}〈001〉) and cube ({100}〈100〉}) texture components. The sharpness of α-fiber, γ-fiber and cube component increases with the increase in rolling reduction from 70 to 85% while that of Goss component decreases. After recrystallization (750 and 800°C), the textures were composed of α and γ-fiber along with significant Goss components. The strength of γ-fiber decreases after annealing. The presence of Goss component in recrystallization textures is attributed to preferential nucleation in {111}〈112〉 type deformed grains. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|