School of Mechanical Engineering, Yonsei University, Seoul 120-749, Republic of Korea
Abstract:
Liquid-phase exfoliation (LPE) is an attractive method for the scaling-up of exfoliated MoS2 sheets compared to chemical vapor deposition and mechanical cleavage. However, the MoS2 nanosheet yield from LPE is too small for practical applications. We report a facile method for the scaling-up of exfoliated MoS2 nanosheets using freeze-dried silk fibroin powders. Compared to MoS2 dispersion in the absence of silk fibroin powder, sonicated MoS2 dispersions with silk fibroin powder (MoS2/Silk dispersion) show noticeably higher exfoliated MoS2 nanosheet yields, with suspended MoS2 concentrations in MoS2/Silk dispersions sonicated for 2 and 5 h of 1.03 and 1.39 mg·mL–1, respectively. The MoS2 concentration in the MoS2/Silk dispersion after centrifugation above 10,000 rpm is more than four times that without the silk fibroin. The size of the dispersed silk fibroin is controlled by the change of centrifugation rate, showing the removal of silk fibroin above tens of micrometers in size after centrifugation at 2,000 rpm. Size-controlled silk fibroin biomolecules combined with MoS2 nanosheets are expected to increase the practical use of such materials in fields related to tissue engineering, biosensors and electrochemical electrodes. Atomic force microscopy and Raman spectroscopy provide the height of the MoS2 nanosheets spin-cast from MoS2 /Silk dispersions, showing thicknesses of 3–6 nm. X-ray photoelectron spectroscopy and X-ray diffraction indicate that the outermost surface layer of the hydrophobic MoS2 crystals interact with oxygen-containing functional groups that exist in the hydrophobic part of silk fibroins. The amphiphilic properties of silk fibroin combined with the MoS2 nanosheets stabilize dispersions by enhancing solvent-material interactions. The large quantities of exfoliated MoS2 nanosheets suspended in the as-synthesized dispersions can be utilized for the fabrication of vapor and electrochemical devices requiring high MoS2 nanosheets contents.