Structure and microwave dielectric properties of the Li2/3(1−x)Sn1/3(1−x)MgxO systems (x = 0‐4/7)
Authors:Zixuan Fang  Bin Tang  Ying Yuan  Xing Zhang  Shuren Zhang
Affiliation:1. National Engineering Center of Electromagnetic Radiation Control Materials, University of Electronic Science and Technology of China, Chengdu, China;2. State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu, China
Abstract:In this paper, the Li2/3(1?x)Sn1/3(1?x)MgxO (LSMxO) ceramic systems were prepared by solid‐state reaction using novel atmosphere‐controlled sintering (x = 0‐4/7). Pure Li2SnO3 was observed for x = 0, the Li2Mg3SnO6 and Li2SnO3 coexisted for x = 1/7, and the coexistence of three kinds of phases was detected for x = 1/5 and 1/4, including Li4MgSn2O7 impurity phase. Pure Li2Mg3SnO6‐like phase with cubic rock salt structure in Fm‐3m space group was obtained in the range of 1/3‐4/7. All samples showed well‐dense and smooth microstructures. The microwave dielectric properties highly depended on the phase composition, bond valence, FWHM of Raman spectrum, Raman shift, average grain sizes, and octahedral distortion. The LSMxO ceramics sintered at 1250°C for 5 hours possessed excellent comprehensive properties of εr = 15.43, Q×f = 80 902 GHz and τf = +5.61 ppm/°C for x = 1/7. Typically, the LSMxO ceramics sintered at 1350°C for 5 hours showed a maximum Q × f of 168 330 GHz for x = 1/2.
Keywords:crystal structures  microstructures  microwave dielectrics ceramics
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号