Effect of notch root radius on fracture toughness of polycrystalline cubic boron nitride |
| |
| Authors: | D Carolan P Alveen A Ivankovi? N Murphy |
| |
| Affiliation: | 1. Cultivating Base for Key Laboratory of Environment-friendly Inorganic Materials in University of Henan Province, School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo, Henan 454000, China;2. Department of Mechanical Engineering, University of North Dakota, Grand Forks, ND 58201, USA;1. State Key Laboratory of Metastable Materials Science & Technology, Yanshan University, Qinhuangdao, Hebei, 066004, P.R. China;2. MOE Engineering Research Center for Brittle Materials Machining, Huaqiao University, Xiamen, 361021, P.R. China |
| |
| Abstract: | The fracture toughness of five grades of polycrystalline cubic boron nitride (PCBN) has been determined using Single Edge V-Notched Beam specimens. Both coarse and fine grade materials were considered, containing CBN grain sizes of between 1 μm and 22 μm. The influence of notch root radius on the measured fracture toughness was examined. The notch root radius was found to have a major effect for materials with smaller CBN grain sizes while only a small effect was noted for the material with large CBN grain sizes. A simple analytical model was developed to explain the effect of the notch root radius on the fracture toughness and was found to agree well with experiment for all the materials tested. It was shown that the effect of notch root radius is directly linked to the size of the CBN grain. It is proposed that this effect results from the interaction between the microstructure and the stress field around the notch tip. |
| |
| Keywords: | |
| 本文献已被 ScienceDirect 等数据库收录！ |
|