Photoluminescence Properties of Color‐Tunable Ca3La6(SiO4)6: Ce3+, Tb3+ Phosphors

A series of newly developed color‐tunable Ca₃La₆(SiO₄)₆: Ce³⁺, Tb³⁺ phosphors were successfully prepared in this study. The crystal structures of the prepared phosphors were revealed to be hexagonal with space group P6₃/m, and the lattice parameters were evaluated via utilizing the Rietveld refinement method. Upon excitation at 288 nm, the emission spectra of Ce³⁺and Tb³⁺ ions co‐doped Ca₃La₆(SiO₄)₆ phosphors included a blue emission band and several emission lines. The blue emission band with a peak at 420 nm originated in the f–d transitions of Ce³⁺ ions, and the emission lines in the range of 450–650 nm were assigned to the ⁵D₄ → ⁷F_J (J = 6, 5, 4, 3) transitions of Tb³⁺ ions. Increasing the doping content of Tb³⁺ ions considerably strengthened Tb³⁺ emission and reduced Ce³⁺ emission owing to the energy transfer from Ce³⁺ to Tb³⁺ ions. The mechanism of the energy transfer was confirmed to be a dipole–dipole interaction. The effective energy transfer from Ce³⁺ to Tb³⁺ ions caused a color shift from purplish‐blue to yellowish‐green. Color‐tunable Ca₃La₆(SiO₄)₆: Ce³⁺, Tb³⁺ phosphors have the potential to be utilized in light‐emitting diodes with proper modulation of the amount of Tb³⁺ ions.