Microwave‐assisted Hydrothermal Synthesis of Single‐crystal Nanorods of Rhabdophane‐type Sr‐doped LaPO4·nH2O

A novel, simple, soft, and fast microwave‐assisted hydrothermal method was used for the preparation of single‐crystal nanorods of hexagonal rhabdophane‐type La_1?xSr_xPO_4?x/2·nH₂O (x = 0 or 0.02) from commercially available La(NO₃)₃·6H₂O, Sr(NO₃)₂, and H₃PO₄. The synthesis was conducted at 130°C for 20 min in a sealed‐vessel microwave reactor specifically designed for synthetic applications, and the resulting products were characterized using a wide battery of analytical techniques. Highly uniform, well‐shaped nanorods of LaPO₄·nH₂O and La_0.98Sr_0.02PO_3.99·nH₂O were readily obtained, with average length of 213 ± 41 nm and 102 ± 25 nm, average aspect ratio (ratio between length and diameter) of 21 ± 9 and 12 ± 5, and specific surface area of 45 ± 2 and 51 ± 1 m²/g, respectively. In both cases, the single‐crystal nanorods grew anisotropically along their c crystallographic‐axis direction. At 700°C, the hexagonal rhabdophane‐type phase has already transformed into the monoclinic monazite‐type structure, although the undoped and Sr‐doped nanorods retain their morphological features and specific surface area during calcination.