Creep of CoO single crystals |
| |
Authors: | A H Clauer M S Seltzer B A Wilcox |
| |
Affiliation: | (1) Metal Science Group, Battelle Memorial Institute, Columbus Laboratories, 505 King Avenue, 43201 Columbus, Ohio, USA |
| |
Abstract: | Cobalt monoxide single crystals having a 100] orientation were creep tested in compression over ranges of temperature, stress and oxygen pressure. The creep curves were S-shaped and only the inflection creep rate, 2, was analysed. In the range of 1000 to 1200° C, 850 to 1700 psi and 10–3 to 1 atm oxygen, 2 was given by 2=A po
2
0.45
7.1exp(– Q
c
/RT) where Q
c
=87±6 kcal/mol at 0.01 atm O
2 and 100±16 kcal/mol at 1 atm O
2. Slip occurred on two orthogonal {011} 0¯11 slip systems. The presence of subboundaries was observed by optical and transmission electron microscopy. It is suggested that the creep rate is controlled by oxygen diffusion. |
| |