| Abstract: | Polybutadiene (PB)/Montmorillonite nanocomposites (NCs) were prepared by in situ polymerization through the anionic polymerization technique. The effects of treating method of organophilic MMT (OMMT), the type of OMMT, and the solvent used in polymerization were studied. The structure and properties of NCs were characterized using X‐ray Diffraction (XRD), transmission electron micrograph (TEM), H‐NMR spectrum, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and dynamic mechanical analysis (DMA). The consumption of BuLi was varied with different treating methods. The molecular weight distribution of PB added with OMMT (DK1) was wide, and the molecular weight distribution became narrow when OMMT‐DK1B and DK4 were added. OMMT did not disperse stably in cyclohexane, but could form a homogeneous solution in toluene and xylene. XRD and TEM showed that exfoliated NCs were obtained by in situ polymerization through the anionic polymerization technique. From the H‐NMR spectrum of PB and PB/OMMT NCs, it could be seen that the content of 1, 2 units of PB increased ～100%, while 1, 4 units decreased when 6.2 wt % of OMMT was added. The results of DSC and DMA indicated that Tg and Tdc were increased when compared with those of PB. Both storage modulus and loss modulus were increased with the addition of OMMT, and tan δ was decreased. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 99: 3615–3621, 2006 |