Surface damage of poly(methylmethacrylate) under fretting loading

The initial fretting damage in a glass/PMMA contact was investigated by means of experiments and numerical (F.E.M.) simulations. Both micro-crack nucleation at the contact edges and particle detachment were identified on the PMMA's surface. Micro-crack initiation was related to the combination of high tensile stresses and positive hydrostatic pressures which are known to enhance crazing. During the early stages of the fretting tests, the distribution of the detached particles within the contact was correlated to the spatial distribution of the cumulative interfacial energy dissipated by friction. As the number of cycles was increased, it was observed that detached particles moved toward the middle of the contact. On the basis of FEM simulations, this particle displacement within the contact was attributed to the existence of differential micro-displacements during the fretting cycle.