Anti-Thermal-Fatigue Property of 8407 Steel With Surface Aluminization and Oxidation Treatment |
| |
Authors: | SUN Jian XU Yu-song WANG Xiao-ming ZOU Zong-shu |
| |
Affiliation: | 1. School of Metallurgy and Materials Science, Jiangsu University of Science and Technology(Zhangjiagang), Zhangjiagang 215600, Jiangsu, China 2. School of Materials Science and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China |
| |
Abstract: | Thermal fatigue failure is one of the main failure forms of 8407 steel. Aiming at improving the anti-thermal-fatigue property of 8407 steel, the method of aluminization and subsequent oxidation is employed to form a complex oxide on the die surface. Thermal fatigue test was performed with the cycle heating method to compare thermal fatigue behaviors of 8407 steel samples with and without aluminization and oxidation treatment. In the test, thermal fatigue crack morphology formed on the surface was observed by scanning electron microscope (SEM) and then variations of initiating rate and propagating rate of main crack of thermal fatigue with cycles were investigated. Moreover, the thermal fatigue property was judged according to thermal fatigue main crack length and its reciprocal. Finally, the anti-thermal-fatigue mechanism of oxide film was clarified. The results show that the surface aluminization and oxidation treatment can improve both the initiating resistance and propagating resistance of thermal fatigue crack, which will improve the anti-thermal-fatigue property of 8407 steel. |
| |
Keywords: | aluminization and oxidation treatment thermal fatigue main crack length crack initiating crack propa-gating |
本文献已被 CNKI 维普 万方数据 ScienceDirect 等数据库收录! |
| 点击此处可从《钢铁研究学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《钢铁研究学报(英文版)》下载全文 |
|