Subsurface damage during dry sliding wear of Al-Al3Ni eutectic alloy

Cylindrical Al-Al₃Ni eutectic alloy wear pins (10 mm in diameter) were slid against a polished steel surface in a pin-on-disc rotating machine under unlubricated conditions with bearing pressures of 6–60 kPa and a constant sliding speed of 70 m min^?1. Metallographic changes in the subsurface region of contact were examined by optical microscopy and microhardness measurements. In the bearing pressure range investigated the alloy exhibited “mild” wear in two linear regions identified as pure “oxidative” wear at low bearing pressures and oxidative with superimposed “metallic” wear at higher bearing pressures. Plastic deformation and fragmentation of the Al₃Ni phase occurred under all bearing pressures. However, in composites prepared by unidirectional solidification containing large Al₃Ni particles fragmentation was insignificant. In all other specimens the size of the fragmented particles in the subsurface region of contact was about 5 μm irrespective of the bearing pressure.