| V型钢导轨表面裂纹分析 |
| |
| 引用本文： | 燕样样.V型钢导轨表面裂纹分析[J].理化检验(物理分册),2005,41(11):585-587. |
| |
| 作者姓名： | 燕样样 |
| |
| 作者单位： | 陕西工业职业技术学院材料系,咸阳,712000 |
| |
| 摘 要： | 对V型钢导轨在热处理后的磨削加工中出现的表面裂纹进行了宏、微观分析，硬度测试及热酸蚀试验。结果表明，磨削不当是导致V型钢导轨出现表面裂纹的主要原因。提出了改进措施。
|
| 关 键 词： | 钢导轨 表面裂纹 磨削裂纹 磨削应力 |
| 文章编号： | 1001-4012（2005）11-0585-03 |
| 收稿时间： | 2004-05-17 |
| 修稿时间： | 2004-05-17 |
SURFACE CRACK ANALYSIS OF V-TYPED STEEL GUIDE |
| |
| YAN Yang-yang.SURFACE CRACK ANALYSIS OF V-TYPED STEEL GUIDE[J].Physical Testing and Chemical Analysis Part A:Physical Testing,2005,41(11):585-587. |
| |
| Authors: | YAN Yang-yang |
| |
| Affiliation: | Materials Science and Engineering, Shaanxi Polytechnic Institute, Xian yang 712000, China |
| |
| Abstract: | V-typed steel guide are the key part in high precision omnipotent tool grinder. After heat treatment, during the grinding process of the guide, cracks are appeared on the surface of most guide. Macroscopic analysis, metallography, hardness testing and heat acid corrosion experiments have been conducted. The results showed that these surface cracks are resulted from improper grinding. Prevention measure was proposed. |
| |
| Keywords: | Steel guide Surface crack Grinding crack Grinding stress |