VC, Cr3C2 doped ultrafine WC-Co cemented carbides prepared by spark plasma sintering

The influence of the addition of 0.3, 0.5 and 0.7 wt.% VC on the density, microstructure and mechanical properties of WC-Cr₃C₂-11 wt.% Co with 0, 0.2, 0.4 and 0.6 wt.% Cr₃C₂ hard metals prepared by spark plasma sintering (SPS) at a temperature of 1200 °C (5 min, 40 MPa) was investigated. Microstructure analysis revealed that the WC grain size in the sintered hard metals was strongly influenced by the VC and Cr₃C₂ content. With the addition of inhibitors and the increased amount of Cr₃C₂, the density is reduced, and on the contrary, the addition of VC as an inhibitor contributes to promoting the densification. The combined addition of Cr₃C₂ and VC could strongly reduce the WC grain growth to about 350 nm. Observation suggests that the fracture of WC-Co cemented carbide is brittle and intergranular. The amount of added VC/Cr₃C₂ should be controlled in a certain range. Samples with an appropriate proportion of VC/Cr₃C₂ added exhibit higher hardness which can be up to 1938 HV₃₀. Toughness, too, can reach 16.34 MPa m^1/2.