Evaluation of Desulphurization Flux in CaO‐Al2O3‐BaO‐CeO2‐MgO System

The flux of the CaO‐Al₂0₃‐BaO‐CeO₂‐MgO system as a desulphurization flux containing no fluorine for the secondary metallurgy process was evaluated in this study. The flux composition was designed using the eutectic compositions of the binary systems. The melting and desulphurization abilities of the fluxes were evaluated by measuring their liquidus temperatures and the distribution ratios of sulphur between the fluxes and the carbon‐saturated iron or stainless steel. The lowest liquidus temperature of 1325°C was obtained by adding 5.7 mass% MgO to the 80mass%A‐20mass%B flux. (A: 12CaO‐7Al₂O₃, B: BaCeO₃+12mass%Al₂O₃). The distribution ratios of sulphur and sulphide capacities of the fluxes in this study were higher than those of the commercial product of calcium aluminate flux. This means that the CaO‐Al₂O₃‐BaO‐CeO₂‐MgO fluxes developed in this study have higher desulphurization and melting abilities compared with the commercial product of calcium aluminate flux.