Synthesis of polyethylene glycol modified carbon dots as a kind of excellent water-based lubricant additives |
| |
Authors: | Xiang Liu |
| |
Affiliation: | College of Civil Aviation Safety Engineering, Civil Aviation Flight University of China, Guanghan, P. R. China |
| |
Abstract: | The polyethylene glycol (PEG) modified carbon dots (CDs-PEG) were facile synthesized by one-pot pyrolysis of the mixture of gluconic acid and PEG. When the average molecular weight of PEG was 200, 600, 1000 and 4000?g/mol, the CDs-PEG were denoted as CDs-PEG200-4000, respectively. As the water-based lubricant additives, the tribological properties of CDs-PEG200 under four-ball mode and steel/steel contact were far superior to PEG200, CDs derived from gluconic acid only, and CDs-PEG600-4000, reflecting the carbon cores and surface groups of CDs-PEG200 should play a synergetic lubrication effect. Specifically, at load of 40?N, adding 0.20?wt% of CDs-PEG200 into base liquid resulted in the largest friction coefficient and wear volume reductions up to 83.5% and 90.9%. Meanwhile, the load carrying capacity of base liquid increased from 50?N to at least 200?N. Amazingly, the lubrication ability of base liquid containing 0.20?wt% of CDs-PEG200 sometimes was even comparable to some lubricant oils. The results of worn surface analyses revealed that the distinguished friction-reducing and antiwear performance of CDs-PEG200 as additives could be attributed to the formed composite lubrication film composed of CDs-PEG200 and Fe3O4 on the rubbing surfaces. |
| |
Keywords: | Carbon dot polyethylene glycol pyrolysis tribological property lubricant additive |
|
|