| 石化行业若干应力腐蚀事例分析 |
| |
| 引用本文： | 安宏,赵声玉. 石化行业若干应力腐蚀事例分析[J]. 腐蚀与防护, 2004, 25(8): 364-366 |
| |
| 作者姓名： | 安宏 赵声玉 |
| |
| 作者单位： | 兰州炼油化工设计院,兰州,730060 |
| |
| 摘 要： | 通过典型事例以及有关腐蚀数据统计分析，论证应力腐蚀失效在化工生产中的危害，同时提出一些改进措施和控制方案。
|
| 关 键 词： | 应力腐蚀开裂 失效 材料 |
| 文章编号： | 1005-748X(2004)08-0364-03 |
| 修稿时间： | 2003-11-18 |
AN ANALYSIS ON SOME TYPICAL CASES OF STRESS CORROSION CRACKING IN PETROCHEMICAL INDUSTRY |
| |
| AN Hong,ZHAO Sheng-yu. AN ANALYSIS ON SOME TYPICAL CASES OF STRESS CORROSION CRACKING IN PETROCHEMICAL INDUSTRY[J]. Corrosion & Protection, 2004, 25(8): 364-366 |
| |
| Authors: | AN Hong ZHAO Sheng-yu |
| |
| Abstract: | Some typical cases of stress corrosion cracking (SCC) in petrochemical industry are reviewed. A statistical analysis is presented to prove the significant damage of such failure. Some improving and controling measures to prevent or reduce the damage are also introduced. |
| |
| Keywords: | Stress corrosion cracking (SCC) Failure Material |