Synthesis,properties, and biodegradability of three-branched copolyamide (4/6)

Previous studies on polyamide 4, excellent properties, functionalities, and biodegradation in natural condition have been shown. In this study, three-branched (star-shaped) copolyamides constituted of polyamide 4 and polyamide 6 constitutional unit were synthesized by anionic ring-opening copolymerization of 2-pyrrolidone with ε-caprolactam. The thermal and mechanical properties and the biodegradability of the obtained copolyamides have been systematically investigated. The weight-average molecular weight of the copolyamides was as high as tens of thousands (M_w 10–80 × 10³ g/mol). The composition of the copolyamides was approximately in accord with the monomer feed ratio, thereby being controllable. The thermal and mechanical properties changed readily as the composition was varied (T_m 146–266°C, ΔH_m 10–70 J/g, T_d 278–369°C, tensile strength 28–64 MPa, elongation at break 80–750%). The copolyamide having 2-pyrrolidone unit of 96–51 mol% exhibited biodegradability by an activated sludge. The biodegradation of the copolyamide proceeded uniformly without disproportion in constitutional unit.