Effect of Sr doped the YFeO3 rare earth ortho-ferrite on structure,magnetic properties,and microwave absorption performance

Given the remarkable performances of rare earth multiferroic ortho-ferrites with magnetic optical and dielectric properties, the Y_1-xSr_xFeO₃ (x = 0, 0.05, 0.1, 0.15) perovskite structure microwave absorbing ferrite materials was successfully synthesized by Sr²⁺ ions A-site doping based on sol-gel technology in this paper. The XRD of all samples was refined with FullProf software, which confirmed the formation of the orthogonal perovskite structure (SG: Pnma). The SEM and TEM results display the average particles size of the samples is distributed between 110 and 160 nm. The increase of Sr doping concentration leads to the increase of particles size, which may be related to the growth of preferred orientation and incomplete substitution. The XPS analysis shows that Fe³⁺ was accompanied by the presence of Fe²⁺ with the doping of Sr²⁺ ions and oxygen vacancies increased significantly. The samples change from weak ferromagnetic state to paramagnetic state with the increase of Sr content. The minimum reflection loss (RL) of the Y_0.95Sr_0.05FeO₃ samples at 12.2 GHz reached ?30.87 dB with thickness of 2.2 mm, where its effective absorption bandwidth (EAB, RL ≤ ?10 dB) reached 2.4 GHz (11.3–13.7 GHz). Moreover, the EAB of the Y_0.85Sr_0.15FeO₃ samples reached 2.64 GHz, and the corresponding range is 9.0–11.6 GHz (X-band).