Tensile properties of hot rolled Mg_(97)Zn_1Y_2 alloy sheets at elevated temperatures

The elevated temperature tensile properties of Mg₉₇Zn₁Y₂ magnesium alloy sheets, hot rolled at 390, 420 and 450 °C respectively, were tested in a temperature range from room temperature to 250 °C with a strain rate of 1.0×10^?3 s^?1. The results show that the variations in yield strength for Mg₉₇Zn₁Y₂ magnesium alloy sheets hot rolled at 390 °C and 420 °C with temperature resemble each other due to their similar morphology of the chain-shaped strengthening phase. The yield strength maintains at a high level of 283 MPa before 200 °C and decreases significantly at 250 °C. Despite of the fine lamellar structure of Mg₉₇Zn₁Y₂ magnesium alloy sheet hot rolled at 450 °C, its yield strength decreases linearly owing to occurrence of the coarse grain, and drops to 239 MPa at 250 °C. The elongation for all hot rolled Mg₉₇Zn₁Y₂ magnesium alloy sheets increases slightly with increasing testing temperature.