Formation and chemical leaching effects of nonequilibrium Al0.6(Fe25Cu75) alloy powder produced by rod milling

The formation and chemical leaching effects of a nonequilibrium Al_0.6(Fe₂₅Cu₇₅)_0.4 powder produced by rod milling is described. X-ray diffraction, transmission electron microscopy, differential scanning calorimetry and vibrating sample magnetometry were used to characterize both the as-milled and leached specimens. After 400 h of milling, only the bcc AlFe phase with an amorphous phase was detected in the XRD patterns. The crystallite size for the bcc AlFe phase (110) after 400 h of milling was about 5.3 nm. The peak temperature and the crystallization temperature of the as-milled powders were 448.7 and 428.0 °C, respectively. Al atoms leaching from the as-milled bcc AlFe powders in the L1 condition did not alter the diffraction pattern significantly, even though Al atoms had been removed. After the L1 specimen was annealed at 500 °C for 1 h, the bcc AlFe phase transformed to the fcc Cu, Fe, and CuFe₂O₄ phases. The peak widths of L1 and L2 specimens were similar, but became broader than that of the as-milled powder. The saturation magnetization decreased with increasing milling time, and a value of 10.4 emu/g was reached after 400 h of milling. After cooling the specimen from 750 °C, the magnetization slowly increased at approximately 491.4 °C, indicating that the bcc AlFe phase had transformed to the fcc Cu and Fe phases.