Relaxor Ferroelectric BaTiO3–Bi(Mg2/3Nb1/3)O3 Ceramics for Energy Storage Application

Perovskite solid solution ceramics of (1 ? x)BaTiO₃–xBi(Mg_2/3Nb_1/3)O₃ (BT–BMN) (x = 0.05–0.2) were synthesized by solid‐state reaction technique. The results show that the BMN addition could lower the sintering temperature of BT‐based ceramics. X‐ray diffraction results reveal a pure perovskite structure for all studied samples. Dielectric measurements exhibit a relaxor‐like characteristic for the BT–BMN ceramics, where broadened phase transition peaks change to a temperature‐stable permittivity plateau (from ?50°C to 300°C) with increasing the BMN content (x = 0.2), and slim polarization–electric field hysteresis loops were observed in samples with x ≥ 0.1. The dielectric breakdown strength and electrical resistivity of BT–BMN ceramics show their maxima of 287.7 kV/cm and 1.53 × 10¹³ Ω cm at x = 0.15, and an energy density of about 1.13 J/cm³ is achieved in the sample of x = 0.1.