Effects of Gd Substitution on Sintering and Optical Properties of Highly Transparent (Y0.95−xGdxEu0.05)2O3 Ceramics

Highly transparent (Y_0.95?xGd_xEu_0.05)₂O₃ (x = 0.15–0.55) ceramics have been fabricated by vacuum sintering at the relatively low temperature of 1700°C for 4 h with the in‐line transmittances of 73.6%–79.5% at the Eu³⁺ emission wavelength of 613 nm (~91.9%–99.3% of the theoretical transmittance of Y_1.34Gd_0.6Eu_0.06O₃ single crystal), whereas the x = 0.65 ceramic undergoes a phase transformation at 1650°C and has a transparency of 53.4% at the lower sintering temperature of 1625°C. The effects of Gd³⁺ substitution for Y³⁺ on the particle characteristics, sintering kinetics, and optical performances of the materials were systematically studied. The results show that (1) calcining the layered rare‐earth hydroxide precursors of the ternary Y–Gd–Eu system yielded rounded oxide particles with greatly reduced hard agglomeration and the particle/crystallite size slightly decreases along with increasing Gd³⁺ incorporation; (2) in the temperature range 1100°C–1480°C, the sintering kinetics of (Y_0.95?xGd_xEu_0.05)₂O₃ is mainly controlled by grain‐boundary diffusion with similar activation energies of ~230 kJ/mol; (3) Gd³⁺ addition promotes grain growth and densification in the temperature range 1100°C–1400°C; (4) the bandgap energies of the (Y_0.95?xGd_xEu_0.05)₂O₃ ceramics generally decrease with increasing x; however, they are much lower than those of the oxide powders; (5) both the oxide powders and the transparent ceramics exhibit the typical red emission of Eu³⁺ at ~613 nm (the ⁵D₀→⁷F₂ transition) under charge transfer (CT) excitation. Gd³⁺ incorporation enhances the photoluminescence and shortens the fluorescence lifetime of Eu³⁺.