Ultra‐low Sintering Temperature Microwave Dielectric Ceramics Based on Na2O‐MoO3 Binary System

The compounds in Na₂O‐MoO₃ system were prepared by the solid‐state reaction route. The phase composition, crystal structures, microstructures, and microwave dielectric properties of the compounds have been investigated. This series of compounds can be sintered well at ultra‐low temperatures of 505°C–660°C. The sintered samples exhibit good microwave dielectric properties, with the relative permittivities (ε_r) of 4.1–12.9, the Q × f values of 19900–62400 GHz, and the τ_f values of ?115 ppm/°C to ?57 ppm/°C. Among the eight compounds in this binary system, three kinds of single‐phase ceramics, namely Na₂MoO₄, Na₂Mo₂O₇ and Na₆Mo₁₁O₃₆ were formed. Furthermore, the relationship between the structure and the microwave dielectric properties in this system has been discussed. The average Na^I‐O and Mo^VI‐O bond valences have an influence on the sintering temperatures in Na₂O‐MoO₃ system. The large valence deviations of Na and Mo lead to a large temperature coefficient of resonant frequency. The X‐ray diffraction and backscattered electron image results show that Na₂MoO₄ doesn't react with Ag and Al at 660°C. Also, Na₂Mo₂O₇ has a chemical compatibility with Al at 575°C.