Synthesis of Nanofiber‐like Mesoporous γ‐Al2O3 toward Its Adsorption Efficiency for Congo Red

Nanofiber‐like mesoporous γ‐Al₂O₃ was synthesized using freshly prepared boehmite sol in the presence of triblock copolymer, P123 following evaporation‐induced self‐assembly (EISA) process followed by calcinations at 400°C–1000°C. The samples were characterized by thermogravimetry (TG), differential thermal analysis (DTA), X‐ray diffraction (XRD), N₂ adsorption–desorption, and transmission electron microscopy (TEM). The adsorption efficiency of the samples with Congo red (CR) was studied by UV – vis spectroscopy. XRD results showed boehmite phase in the as‐prepared sample while γ‐Al₂O₃ phase obtained at 400°C was stable up to 900°C, a little transformation of θ‐Al₂O₃ resulted at 1000°C. The Brunauer‐Emmett‐Teller surface area of the 400°C‐treated sample was found to be 175.5 m²g ^{? 1}. The TEM micrograph showed nanofiber‐like morphology of γ‐Al₂O_3. The 400°C‐treated sample showed about 100% CR adsorption within 60 min.