Low Temperature Synthesis of Needle‐like α‐FeOOH and Their Conversion into α‐Fe2O3 Nanorods for Humidity Sensing Application

In this study, we report template and surfactant‐free, low temperature (70°C) synthesis of needle‐like α‐FeOOH and its conversion at 400°C into α‐Fe₂O₃ nanorods using Fe(+2) and Fe(+3) chlorides and urea as a hydrolysis‐controlling agent. The isolated needle‐like α‐FeOOH indicates asparagus‐type growth pattern having length ca. 600 nm with 80 nm diameter at base and apex diameter of around 10 nm. The sample on heating (α‐Fe₂O₃) shows nanorod‐like morphology. The samples were characterized using various physicochemical characterization techniques such as XRD, Raman spectroscopy, UV‐Vis spectroscopy, particle size distribution analysis, Field Emission Scanning Electron Microscopy (FE‐SEM), and humidity sensing performance. The humidity sensing behavior of both α‐FeOOH and α‐Fe₂O₃ was studied. The α‐FeOOH shows quicker (10 s) and higher response toward change in humidity from 20%RH to 90%RH as compared with α‐Fe₂O₃ (60 s). Their typical morphology and crystalline structure plays an important role in humidity sensing behavior.