| P(MMA-AN)/TiO2复合粒子的制备及光催化性能 |
| |
| 引用本文： | 潘柯良,朱云峰,江龙,杨明娇,刘舒扬,淡宜.P(MMA-AN)/TiO2复合粒子的制备及光催化性能[J].高分子材料科学与工程,2007,23(5):163-166. |
| |
| 作者姓名： | 潘柯良 朱云峰 江龙 杨明娇 刘舒扬 淡宜 |
| |
| 作者单位： | 高分子材料工程国家重点实验室(四川大学),四川大学高分子研究所,四川,成都,610065;高分子材料工程国家重点实验室(四川大学),四川大学高分子研究所,四川,成都,610065;高分子材料工程国家重点实验室(四川大学),四川大学高分子研究所,四川,成都,610065;高分子材料工程国家重点实验室(四川大学),四川大学高分子研究所,四川,成都,610065;高分子材料工程国家重点实验室(四川大学),四川大学高分子研究所,四川,成都,610065;高分子材料工程国家重点实验室(四川大学),四川大学高分子研究所,四川,成都,610065 |
| |
| 摘 要： | 采用原位乳液聚合方法制备了基于共价键结合的P(MMA-AN)/TiO2复合粒子,红外光谱和热失重分析结果表明P(MMA-AN)在TiO2表面接枝率为15.9%。以甲基橙溶液为目标污染物,研究了P(MMA-AN)/TiO2复合粒子和TiO2对甲基橙的吸附和光催化降解甲基橙溶液的性能,结果表明:两种粒子对甲基橙的吸附都很少;在相同时间内,P(MMA-AN)/TiO2复合粒子对甲基橙溶液的降解性能优于TiO2,紫外光照180 min后,P(MMA-AN)/TiO2复合粒子对甲基橙溶液的降解率达到了88%,而TiO2仅为74%。
|
| 关 键 词： | TiO2 P(MMA-AN)/TiO2复合粒子 乳液聚合 光催化 |
| 文章编号： | 1000-7555（2007）05-0163-04 |
| 修稿时间： | 2007-03-09 |
Studies on Preparation and Photocatalytic Activity of P(MMA-AN)/TiO2 Composite Particles |
| |
| PAN Ke-liang,ZHU Yun-feng,JIANG Long,YANG Ming-jiao,LIU Shu-yang,DAN Yi.Studies on Preparation and Photocatalytic Activity of P(MMA-AN)/TiO2 Composite Particles[J].Polymer Materials Science & Engineering,2007,23(5):163-166. |
| |
| Authors: | PAN Ke-liang ZHU Yun-feng JIANG Long YANG Ming-jiao LIU Shu-yang DAN Yi |
| |
| Affiliation: | State Key Laboratory of Polymer Materials Engineering of China (Sichuan University |
| |
| Abstract: | The P(MMA-AN)/TiO2 composite particles were prepared by in-situ emulsion polymerization of the monomers in the presence of anatase TiO2 which was modified by silane coupling agent to ensure that the P(MMA-AN) can combine with TiO2 by chemical bonds.According to IR and TGA results,the P(MMA-AN)/TiO2 composite particles are successfully prepared and the percentage of grafting is 15.9%.The methyl orange(MO) solution was used as target pollutant to study the photocatalytic activity of P(MMA-AN)/TiO2 composite particles and TiO2.The research results indicate that the P(MMA-AN)/TiO2 behaves the higher photocatalytic activity than the TiO2. Especially,the degrading ration of MO under UV irradiation after 180 min reaches 88% by P(MMA-AN)/TiO2,while only 74% by TiO2. |
| |
| Keywords: | TiO2 P(MMA-AN)/TiO2 composite particles emulsion polymerization photocatalysis |