| Abstract: | Nanocomposites of epoxy resin with montmorillonite clay were synthesized by swelling of different proportions of the clay in a diglycidyl ether of bisphenol‐A followed by in situ polymerization with aromatic diamine as a curing agent. The montmorillonite was modified with octadecylamine and made organophilic. The organoclay was found to be intercalated easily by incorporation of the epoxy precursor and the clay galleries were simultaneously expanded. However, Na‐montmorillonite clay could not be intercalated during the mixing or through the curing process. Curing temperature was found to provide a balance between the reaction rate of the epoxy precursor and the diffusion rate of the curing agent into the clay galleries. The cure kinetics were studied by differential scanning calorimetry. The exfoliation behavior of the organoclay system was investigated by X‐ray diffraction. Thermogravimetric analysis was used to determine the thermal stability, which was correlated with the ionic exchange between the organic species and the silicate layers. The morphology of the nanocomposites was evaluated by scanning electron microscopy. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2201–2210, 2004 |