基于组织均匀性的690合金管冷轧及退火工艺优化
引用本文:杨亮, 董建新, 何智勇, 张麦仓. 基于组织均匀性的690合金管冷轧及退火工艺优化[J]. 工程科学学报, 2012, 34(4): 410-416. DOI: 10.13374/j.issn1001-053x.2012.04.005
作者姓名:杨亮  董建新  何智勇  张麦仓
作者单位:1.北京科技大学材料科学与工程学院, 北京 100083
基金项目:国家自然科学基金;国家高技术研究发展计划(863计划)
摘    要:针对国产690合金成品管晶粒组织均匀性控制差的问题,引入不均匀因子Z评定组织均匀性,设计单、双道次冷轧和退火实验.实验结果表明:690合金荒管经变形量50%的单道次冷轧,在1100℃下保温5 min的中间退火处理后晶粒组织最均匀;荒管经一二道次变形量依次为50%、70%的双道次冷轧,两道冷轧工序之间采用1100℃保温时间5 min的中间退火,最后在1060℃下保温5 min或者1100℃保温3 min进行固溶处理获得的组织均匀性最好.

关 键 词:镍基合金  无缝钢管  冷轧  退火  显微组织
收稿时间:2011-03-04

Optimization design of cold rolling and annealing processes for 690 alloy tubes based on microstructure uniformity
YANG Liang, DONG Jian-xin, HE Zhi-yong, ZHANG Mai-cang. Optimization design of cold rolling and annealing processes for 690 alloy tubes based on microstructure uniformity[J]. Chinese Journal of Engineering, 2012, 34(4): 410-416. DOI: 10.13374/j.issn1001-053x.2012.04.005
Authors:YANG Liang  DONG Jian-xin  HE Zhi-yong  ZHANG Mai-cang
Affiliation:1.School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China
Abstract:Single and double-pass cold rolling and annealing tests were carried out aiming at the poor control of grain size uniformity for 690 alloy tubes in China.A heterogeneous factor Z was introduced to evaluate the uniformity of microstructures.The results show that the grain size is most homogeneous in 690 alloy pierced billets by single-pass cold rolling with a deformation of 50% and annealing at 1 100℃ for a holding time of 5 min.The best uniform grain size distribution can be obtained by the first pass cold rolling with a deformation of 50%,the second pass cold rolling with a deformation of 70%,and annealing at 1 100℃ for a holding time of 5 min between the two cold rolled processes,followed by solution heat treatment at 1 060℃ for 5 min or 1 100℃ for 3 min. 
Keywords:nickel base alloys  seamless tubes  cold rolling  annealing  microstructure