| 超低碳深冲钢卷曲温度实验室研究 |
| |
| 作者姓名： | 屈啸 彭伟 许晓嫦 裴斐 |
| |
| 作者单位： | 1. 中南大学材料科学与工程学院, 长沙 410083; |
| |
| 摘 要： | 利用Gleeble-1500试验机、X射线衍射仪、金相显微镜和透射电镜等手段,研究了卷曲温度对一种超低碳深冲钢显微组织、纳米级析出相和相应冷轧退火板织构的影响,并且获得了最佳的卷曲温度.热轧板中的析出相主要是硫化铜以及硫化铜和硫化锰复合析出物.低温卷曲时,析出相数量少、尺寸较大且分布稀疏.为获得较强的有利织构和良好的冲压性能,实验钢卷取温度应选定在600℃以下.
|
| 关 键 词： | 低碳钢 深冲 卷曲温度 纳米级 析出相 织构 |
| 收稿时间： | 2011-08-26 |
Laboratory studies on the coiling temperature of ultra-low carbon deep drawing steel |
| |
| Affiliation: | 1. College of Material Science and Engineering, Central South University, Changsha 410083, China;2. VALIN Lianyuan Iron & Steel Group Co. Ltd., Loudi 417009, China |
| |
| Abstract: | The effects of coiling temperature on the microstructure and nano-scaled precipitates of ultra-low carbon steel with deep drawability, together with the corresponding textures of the annealed cold-rolled sheet, were investigated by Gleeble-1500 hot simulator, X-ray diffraction, optical microscopy and transmission electron microscope. It is found that nano-scaled precipitates in the hotrolled steel sheet are mainly CuS and CuS-MnS. The precipitates are less, coarse, and sparse when the coiling temperature is lower. To obtain a strong favorable texture and a better drawing property, the best coiling temperature should be under 600℃. |
| |
| Keywords: | |
| 本文献已被 万方数据 等数据库收录！ |
| 点击此处可从《》浏览原始摘要信息 |
|
点击此处可从《》下载全文 |
|