Measurement of Porosity in Ceramic Coatings by Thermogravimetric Volatilization of Liquids |
| |
Authors: | Bradley D Craig Lorraine F Francis Lloyd Abrams |
| |
Affiliation: | Department of Chemical Engineering and Materials Science, University of Minnesota, Minneapolis, Minnesota 55455;Central Research and Development, DuPont Chemical Company, Wilmington, Delaware 19880 |
| |
Abstract: | A simple gravimetric method was developed to determine the open porosity in ceramic coatings. The coating's pore space was filled with a liquid and the weight loss on volatilization of the liquid was measured in a thermogravimetric analyzer. This thermogravimetric volatilization of liquids (TVL) method was used to characterize the porosity in titania coatings, alumina/aluminum phosphate coatings, and free-standing films of alumina. Several liquids were used; ethylene glycol and 1,3-propanediol gave the best results due to their low volatilities at room temperature. The measured porosities of the ceramic coatings ranged from 30% to 80% and the pore sizes (as determined by SEM and mercury porosimetry) ranged from 0.1 to 15 μm. The standard deviation of the TVL measurement was smaller for thicker coatings (e.g., ≥20 μm). Porosities determined by TVL were within typically 5-10% of those determined by mercury intrusion porosimetry on identical samples. Characterization of a series of alumina/aluminum phosphate coatings showed a decrease in porosity consistent with expectations based on density and SEM observations. TVL is nondestructive, can be used for small volumes of sample, and when combined with SEM, provides a good means to characterize coating porosity and pore structure. |
| |
Keywords: | |
|
|