Joining of Cf-SiC composites and ZrB2-SiC based composites for ultra high temperature applications

Gas tungsten arc welding (GTAW) of Cf–SiC composites to themselves and to ZrB₂-SiC based composites have been carried out with a filler material of (ZrB₂-SiC-B₄C-Y₂O₃-Al₂O₃) composite. The weld interfaces of joints of composites were clean and free from porosity and cracks. Penetration of filler material into voids and pores existing in the Cf-SiC composites was observed. An average shear strength of 25.7?MPa was achieved. The ZrB₂-SiC based composite joined to Cf-SiC (CVD) composite was exposed for 300?s to the oxy-propane flame at 2300?°C. The joint and interfaces between the filler material and parent composites were found to be unaffected by thermal cycling and oxidation during the exposure to the oxy-propane flame.