Effect of Y2O3 on the oxidation properties of ZrSi2/SiC coating prepared by SAPS on the carbon-carbon composites

In order to improve the oxidation resistance of carbon-carbon (C/C) composites at high temperature, different content of Y₂O₃ modified ZrSi₂/SiC coating for C/C composites were prepared by pack cementation and supersonic atmosphere plasma spraying (SAPS). Microstructure observation and phase identification of the coatings were analyzed by SEM, XRD, DSC/TG and EDS. Experimental results shown that the coating with 10?wt% Y₂O₃ effectively protected C/C composites from oxidation at 1500?°C in air for 301?h with a mass loss of 0.13% and experienced 18 thermal shock times from room temperature (RT) to 1500?°C. First, Y₂O₃ could restrain the phase transition of ZrO₂ to reduce the formation of thermal stresses of the coating; second, the random distribution of ZrO₂ ceramic particles and the formation of ZrSiO₄ enhanced the stability of the SiO₂; third, the formation of Y₂Si₂O₇ and Y₂SiO₅ could relieve the thermal mismatch between ZrSi₂-Y₂O₃ outer layer and the inner layer.