Mechanical and thermal properties of LaMgAl11O19 |
| |
| Authors: | B. Jiang Z.H. Huang Y.G. Liu P. Peng J. Zhang |
| |
| Affiliation: | School of Materials Science and Technology, China University of Geosciences (Beijing), No. 29 Xueyuan Road, Beijing 100083, People's Republic of China |
| |
| Abstract: | Lanthanum magnesium hexaaluminate (LaMgAl11O19) powders were synthesized successfully at 1300 °C for 4 h by solid-state reaction, and LaMgAl11O19 ceramic was prepared at 1700 °C for 6 h by pressureless sintering. Phase composition, microstructure, mechanical and thermophysical properties of LaMgAl11O19 ceramic were investigated. Results show that the flexural strength and fracture toughness of LaMgAl11O19 ceramic are 353.3 ± 12.5 MPa and 4.60 ± 0.46 MPa m1/2. Young's Modulus and Poisson ratio is 295 GPa and 0.23, respectively. The linear thermal expansion coefficient of LaMgAl11O19 ceramic from 473 K to 1473 K is 9.17 × 10−6/K, and thermal conductivity at 1273 K is 2.55 W/m K. |
| |
| Keywords: | A. Inorganic compounds D. Microstructure D. Mechanical properties D. Thermal conductivity |
| 本文献已被 ScienceDirect 等数据库收录！ |
|