| 钢丸增强ZA27复合材料的制备与摩擦磨损特性 |
| |
| 引用本文： | 吴执成,张军.钢丸增强ZA27复合材料的制备与摩擦磨损特性[J].特种铸造及有色合金,1997(6):12-14. |
| |
| 作者姓名： | 吴执成 张军 |
| |
| 作者单位： | 华中理工大学 |
| |
| 摘 要： | 采用搅溶加压铸造研制了钢丸增强ＺＡ２７复合材料（ＺＳＣ），复合工艺简便，ＺＳＣ组织致密，钢丸与基体呈冶金结合，切削加工性能良好；在干摩擦和油润条件下，ＺＳＣ的耐磨性随钢丸量的增加而增加，并优于相同试验条件下的ＺＡ２７合金；干摩擦下ＺＳＣ具有自润滑能力和良好的耐磨减摩性能，油润下随滑动速度和载荷的增大其耐磨性较ＺＡ２７更具优势。
|
| 关 键 词： | 复合材料 钢丸 高铝锌基合金 摩擦磨损 显微组织 |
Fabrication and Friction Wear Properties of Steel Shot Reinforced ZA27 Composite |
| |
| Wu Zhicheng,Zhang Jun,Duan Hanqiao,Gao Jianhua.Fabrication and Friction Wear Properties of Steel Shot Reinforced ZA27 Composite[J].Special Casting & Nonferrous Alloys,1997(6):12-14. |
| |
| Authors: | Wu Zhicheng Zhang Jun Duan Hanqiao Gao Jianhua |
| |
| Affiliation: | Huazhong University of Science and Technology |
| |
| Abstract: | The steel shot reinforced ZA27 composite (ZSC in brief) which was fabricated easily by stirring melt and pressure casting process had a compact structure and good machinability. The steel shots combined with ZA27 matrix metallurgically. The wear resisting and antifriction properties of ZSC increased as the amount of steel shots increasing and were better than that of ZA27 under same conditions. ZSC had a self lubricating ability when there was no lubrication and under oil lubrication its wear resisting property was more excellent when friction rate and load increased. |
| |
| Keywords: | Composite Steel Shot ZA27 Alloy Friction Wear Microstructure |