Synthesis and characterization of polyimides based on isopropylidene-containing bis(ether anhydride)s

Two bis(ether anhydride)s, 4,4′-1,4-phenylenebis(isopropylidene-1,4-phenyleneoxy)]-diphthalic anhydride (IV _a) and 4,4′-isopropylidenebis(1,4-phenylene)dioxy]diphthalic anhydride (IV _b), were prepared in three steps starting from the nucleophilic nitrodisplacement reaction of 4-nitrophthalonitrile with α,α ′-bis(4-hydroxyphenyl)-1,4-diisopropylbenzene (I _a) and 4,4′-isopropylidenediphenol (I _b) in N,N-dimethylformamide (DMF) in the presence of potassium carbonate. The bis(ether anhydride)s IV _a and IV _b were polymerized with various aromatic diamines to obtain two series of poly(ether amic acid)s VI _a–g and VII _a–g with inherent viscosities in the range of 0.30∼0.74 and 0.29∼1.01 dL/g, respectively. The poly(ether amic acid)s were converted to poly(ether imide)s VIII _a–g and IX _a–g by thermal cyclodehydration. Most of the poly(ether imide)s could afford flexible and tough films, and they showed high solubility in polar solvents such as N-methyl-2-pyrrolidone (NMP), N,N-dimethylacetamide, and m-cresol. The obtained poly(ether imide) films had tensile strengths of 45∼83 MPa, elongations-to-break of 6∼27%, and initial modulus of 0.6∼1.7 GPa. The T_gs of poly(ether imide)s VIII _a–g and IX _a–g were in the range of 194∼210 and 204∼243 °C, respectively. Thermogravimetric analysis (TG) showed that 10% weight loss temperatures of all the polymers were above 500 °C in both air and nitrogen atomspheres.