Homogeneity Region of Strontium- and Magnesium-Containing LaGaO3 at Temperatures between 1100° and 1500°C in Air

Phase stability studies were performed within the quasi-ternary system LaGaO₃-SrGaO_2.5-"LaMgO_2.5". Emphasis was cast on the temperature dependence of the homogeneity region of La_{1? x} Sr _x Ga_{1? y} Mg _y O_3?δ perovskite solid solutions. Isothermal sections were determined at 1100°, 1250°, 1400°, and 1500°C in a static air atmosphere. The single-phase homogeneity region was found to considerably diminish with decreasing temperature, indicating a reduction of the solid solubility of Sr and Mg, and below 1100°C the doped perovskite becomes unstable. Consequently, the cubic perovskite phase was found to exist only at elevated temperatures and for high Sr and Mg amounts. Sample preparation was performed by the mixed-oxide process as well as by a modified combustion synthesis.