High Cr white cast iron/carbon steel bimetal liner by lost foam casting with liquid-liquid composite process |
| |
Authors: | Xiao Xiaofeng Ye Shengping Yin Weixin Zhou Xiaoguang Xue Qiong |
| |
Affiliation: | 1. State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, China; School of Mechanical Engineering and Automation, Wuhan Textile University, Wuhan 430073, China 2. State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, China 3. Wuhan ZhiKe Abrasive-Resistant Material S&T Development Co., Ltd, Wuhan 430073, China 4. College of Science, Wuhan University of Technology,Wuhan 430079, China |
| |
Abstract: | Liners in wet ball mill for mineral processing industry must bear abrasive wear and corrosive wear, and consequently,the service life of the liner made from traditional materials,such as Hadfield steel and alloyed steels,is typically less than ten months.Bimetal liner,made from high Cr white cast iron and carbon steel,has been successfully developed by using liquid-liquid composite lost foam casting process.The microstructure and interface of the composite were analyzed using optical microscope,SEM,EDX and XRD.Micrographs indicate that the boundary of bimetal combination regions is staggered like dogtooth,two liquid metals are not mixed,and the interface presents excellent metallurgical bonding state.After heat treatment,the composite liner specimens have shown excellent properties,including hardness>61 HRC,fracture toughnessα k >16.5 J·cm-2 and bending strength >1,600 MPa.Wear comparison was made between the bimetal composite liner and alloyed steel liner in an industrial hematite ball mill of WISCO,and the results of eight-month test in wet grinding environment have proved that the service life of the bimetal composite liner is three times as long as that of the alloyed steel liner. |
| |
Keywords: | bimetal liner liquid-liquid composite process lost foam casting high Cr white cast iron |
本文献已被 CNKI 万方数据 等数据库收录! |
|