Industrial Atmospheric Corrosion Resistance of P-RE Weathering Steel |
|
| Authors: | MI Feng-yi WANG Xiang-dong LIU Zhi-pu WANG Bing PENG Yun TAO Dong-ping |
| Affiliation: | 1. Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology, Kunming 650093,Yunnan, China; Division of Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China 2. Division of Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China 3. Benxi Iron and Steel Group Limited Company, Benxi 117000, Liaoning, China 4. Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology, Kunming 650093,Yunnan, China |
| Abstract: | The corrosion behavior of low-carbon steel (CS), P-bearing steel (PS) and P-RE weathering steel (P-REWS)exposed for two years in Jiangjin of China was investigated. The results showed that during 2-year exposure test,corrosion data of the experimental steels followed the bilogarithmic equation, and the average corrosion depth of PS and P-REWS was decreased by 19.5% and 28.2% respectively compared with that of CS. Scanning electron microscope, electrochemical impedance spectroscope and Fourier transform infrared spectroscope were used to characterize the corrosion products. The research results showed that P in steel could promote the formation of an amorphous ferric oxyhydroxide layer near the substrate. The addition of RE could effectively increase the charge transportation resistance of rust. |
| Keywords: | weathering steel industrial atmosphere rust layer synergistic effect |
| 本文献已被 维普 万方数据 ScienceDirect 等数据库收录！ | |
| 点击此处可从《钢铁研究学报(英文版)》浏览原始摘要信息 | |
| 点击此处可从《钢铁研究学报(英文版)》下载全文 | |