Performance of biomimetic coating modified fiber incorporated styrene butadiene styrene modified asphalt

This study reports the effect of polydopamine bionic coating and γ-methacryloxypropyltrimethoxysilane (KH570) composite modified polyacrylonitrile (PAN) fiber as a secondary modifier on the performance of styrene-butadiene-styrene (SBS) modified asphalt. Dynamic shear rheometer test indicated the complex shear modulu, storage modulus, and loss modulus of modified PAN (KD-PAN) incorporated SBS modified asphalt was increased by 12.4, 20.5, and 11.2%, respectively compared with PAN/SBS modified asphalt. The master curve of G^* of fiber/SBS composite modified asphalt shows that the deformation resistance of KD-PAN/SBS modified asphalt is greater than that of PAN/SBS modified asphalt in the entire loading frequency range. The cone penetration test showed significantly enhanced shear strength of KD-PAN/SBS modified asphalt. The adhesion work test results and SEM images of interface between fiber and SBS modified asphalt revealed that the adhesion effect of KD-PAN and SBS modified asphalt is better than that of PAN and SBS modified asphalt. SEM and AFM images of fiber further showed that the fiber surface becomes rough after modification. The increased surface roughness of KD-PAN facilitated the adherence of SBS modified asphalt to it, which in turn led to the enhanced performance of KD-PAN/SBS composite modified asphalt at the same fiber content and temperature.