Interface characterization and thermal degradation of ferrite/poly(vinylidene fluoride) multiferroic nanocomposites

Flexible multiferroic 0–3 composite films, with CoFe₂O₄, Ni_0.5Zn_0.5Fe₂O₄ or NiFe₂O₄ ferrite nanoparticles as filler and polyvinylidene fluoride (PVDF) as the polymer matrix, have been prepared by solvent casting and melt crystallization. The inclusion of ferrite nanoparticles in the polymer allows to obtain magnetoelectric nanocomposites through the nucleation of the piezoelectric β-phase of the polymer by the ferrite fillers. Since the interface between PVDF and the nanoparticles has an important role in the nucleation of the polymer phase, thermogravimetric analysis was used in order to identify and quantify the interface region and to correlate it with the β-phase content. It is found that an intimate relation exists between the size of the interface region and the piezoelectric β-phase formation that depends on the content and type of ferrite nanoparticles. The interface value and the β-phase content increase with increasing ferrite loading and they are higher for CoFe₂O₄ and Ni_0.5Zn_0.5Fe₂O₄ ferrite nanoparticles. The composites shows lower thermal stability than the pure polymer due to the existence of mass loss processes at lower temperature than the main degradation of the polymer. The main degradation of the polymer matrix, nevertheless, shows increased degradation temperature with increasing ferrite content.