全硅MCM-41中孔分子筛的合成

在碱性条件下，采用水热晶化法，以水玻璃为硅源，表面活性剂十六烷基三甲基溴化铵为结构模板剂，成功合成出全硅MCM－41中孔分子筛。采用X射线衍射分析研究了合成条件(pH值）、凝胶配比（表面活性剂／SiO2、H2O/SiO2）和凝胶后处理条件（老化时间、晶化温度、晶化时间和焙烧温度）对MCM－41结构的影响。结果表明全硅MCM－41的合成条件为pH10.5-12.5，表面活性剂／SiO20.05-0.7，H2O/SiO2 40－200，老化时间长对合成晶形较的全硅MCM－41有利。晶化温度70℃-100℃，晶化时间24小时，焙烧温度540℃－740℃。

Synthesis of Silica Mesoporous Molecular Sieve MCM-41

Under the alkaline condition，the synthesis of mesoporous molecular sieves MCM-41 had been accomplished successfully in a hydrothermal system using sodium silicate as the source of silicon and surfactant C16H33(CH3)3NBr as structural template. The technique of X-Ray Diffraction was used to identify the effects of the systhesis pH condition，the composition of gel (surfactant/SiO2，H2O/SiO2) and treating conditions of gel (aging time, crystralizing temperature, crystralizing time, calcined temperature) on the crystral structure of MCM-41. The results showed that the synthesis conditions for getting suitable mesoporous molecular sieves MCM-41 are pH=10.5~12.5, surfactant/SiO2=0.05~0.7, H2O/SiO2=40~200, aging time as long as possible, crystralizing temperature 70℃~100℃, crystralizing time 24 hours and calcined temperature 540℃~740℃。