Effect of adding different percentages of HfCl4 on the hydrogen storage properties of MgH2

Magnesium hydride (MgH₂) is the best candidate material to store hydrogen in the solid-state form owing to its advantages such as good reversibility, high hydrogen storage capacity (7.6 wt%), low raw material cost and abundance in the earth. Nevertheless, slow desorption/absorption kinetics and high thermodynamic stability are two issues that have constrained the commercialization of MgH₂ as a solid-state hydrogen storage material. So, to boost the desorption/absorption kinetics and to alter the thermodynamics of MgH₂, hafnium tetrachloride (HfCl₄) was used as a catalyst in this study. Different percentages of HfCl₄ (5, 10, 15 and 20 wt%) were added to MgH₂ and their catalytic influences on the hydrogen storage properties of MgH₂ were investigated. Results showed that the 15 wt% HfCl₄-doped MgH₂ sample was the best composite to enhance the hydrogen storage performance of MgH₂. The onset decomposition temperature of the 15 wt% HfCl₄-doped MgH₂ composite was decreased by ~75 °C compared to as-milled MgH₂. Meanwhile, the desorption/absorption kinetic measurements showed an improvement compared to the undoped MgH₂. From the Kissinger analysis, the apparent dehydrogenation activation energy was 167.0 kJ/mol for undoped MgH₂ and 102.0 kJ/mol for 15 wt% HfCl₄-doped MgH₂. This shows that the HfCl₄ addition reduced the activation energy of the hydrogen decomposition of MgH₂. The desorption enthalpy change calculated by the van't Hoff equation showed that the addition of HfCl₄ to MgH₂ did not affect the thermodynamic properties. Scanning electron microscopy showed that the size of the MgH₂ particles decreased and there was less agglomeration after the addition of HfCl₄. It is believed that the decrease in the particle size and in-situ generated MgCl₂ and Hf-containing species had synergistic catalytic effects on enhancing the hydrogen storage properties of the HfCl₄-doped MgH₂ composite.