Modified La0.6Sr0.4Co0.2Fe0.8O3-δ cathodes with the infiltration of Er0.4Bi1.6O3 for intermediate-temperature solid oxide fuel cells

Aiming to lower the activation energy and expedite the oxygen reduction reaction (ORR) process of La_0.6Sr_0.4Co_0.2Fe_0.8O_3-δ (LSCF) cathodes for application in intermediate-temperature solid oxide fuel cells (IT-SOFCs), Er_0.4Bi_1.6O₃ (ESB) modified LSCF was prepared by infiltrating using organic solvents. The infiltration of ESB dramatically reduces the polarization resistances of LSCF cathodes (from 0.27 to 0.11 Ω cm² at 700 °C, from 0.58 to 0.25 Ω cm² at 650 °C), and lowers their activation energy (from 100.28 to 97.15 kJ mol^?1). Also, ESB makes the rate-limiting step of LSCF cathodes at high frequency change from the charge transfer process on the cathode to the adsorption and diffusion of oxygen on cathode surface. The single cell with ESB infiltrated LSCF cathodes shows a peak power density of 469 mW cm^?2 at 700 °C using humid hydrogen and air as fuels and oxidants, respectively, as well as a good short-term stability for 50 h.