Synthesis and characterization of long-side-chain type quaternary ammonium-functionalized poly (ether ether ketone) anion exchange membranes |
| |
Authors: | Hui Wang Xinming Du Hongyu Zhang Hongcheng Shen Qian Liu Zhe Wang |
| |
Affiliation: | 1. School of Chemistry and Life Science, Changchun University of Technology, Changchun, 130012, China;2. College of Chemical Engineering, Changchun University of Technology, Changchun, 130012, China;3. Advanced Institute of Materials Science Changchun University of Technology, Changchun, 130012, China |
| |
Abstract: | A series of quaternary ammonium salt poly(ether ether ketone) AEMs containing long ether substituents are successfully prepared, and their chemical structure is confirmed by 1H NMR and FT-IR. The distinct microphase separation morphology of AEMs is observed by TEM. As the content of methylhydroquinone increases, the ion conductivity of AEMs gradually increases. When the content of methylhydroquinone increases to 80%, the hydroxide conductivity of PEEK-DABDA-80 membrane reaches 0.052 S/cm at 80 °C. Meanwhile, it exhibits excellent mechanical properties and anti-swelling ability, with tensile strength of 25 MPa, elongation at break of 8.12% and swelling ratio is only 17.4% at 80 °C. And AEMs also display the better thermal stability. After soaked in 1 M NaOH at 60 °C for 30 days, PEEK-DABDA-80 membrane shows acceptable ion conductivity of 0.021 S/cm at 60 °C. In view of these properties, PEEK-DABDA-x AEMs may display potential application as alkaline AEMs. |
| |
Keywords: | 4-(dimethylamino)butyraldehyde diethyl acetal Anion exchange membrane Poly(ether ether ketone) Conductivity Alkaline stability |
本文献已被 ScienceDirect 等数据库收录! |
|